Fournisseur et exportateur de tubes sans soudure ASTM A312 en vrac | KXINOX

Tube sans soudure en acier inoxydable/

  1. Accueil
  2. Produits
  3. Tube sans soudure en acier inoxydable
  4. ASTM A312 Tube en acier inoxydable sans soudure
ASTM A312 Tuyau sans soudure en acier inoxydable

ASTM A312 Tube en acier inoxydable sans soudure

Nom：Tuyau sans soudure en acier inoxydable ASTM A312

Taille :1/2"-36"inch DN5~DN1000,OD6mm-OD1020mm

Matériau :SS 304/SS316L Tp304/304L,TP316/316L,Tp310S,Tp347h,904L,Uns S32750,SAF2507,UNS32760,UNS32205,UNS S31803

Type de connexion :SOUDURE/THREAD

Pression de travail :1,6Mpa/2,5mpa/5mpa

Plage d'épaisseur :SCH 5, SCH10, SCH 40, SCH 80, SCH 80S, SCH 160, SCH XXH, SCH XXS, SCH XS

Traitement de surface :Décapage/Polissage/Recuit brillant/EP/MP/Nealed and Pickled (AP), Polished, Bright Annealed (BA), Cold Drawn, MF

État fini：Sans soudure / ERW / Soudé / Fabriqué / CDW / CDS / DOM / CEW / 100% Soudé aux rayons X

Application :Système de canalisation de contrôle des fluides

Numéro de modèle : A312

Orignal :Wenzhou, Zhejiang

Standard :EU,JIS, AiSi, ASTM, DIN ,GOST,EN ,ASTM A213, ASTM A312, ASTM A269, ASTM A778, ASTM A554, ASTM A249, ASTM A269, ASTM A270, ASTM A789, DIN 17456, DIN17457, DIN 17459, JIS G3459, JIS G3463, GOST9941, EN10216, BS3605, GB13296,Acord requiment cad drawing

Marque :OEM Ava

Technique:Presselible

Utilisation :Tube rond

Paquet :Emballage standard pour l'exportation

Prix：Négocier 1000~12000 usd/tonne

Livraison：Accord Quantité

Certificat：

ABS, GL, DNV, NK, PED, AD2000, GOST9941-81, CCS, ISO 9001-2008

Capacité de production：1 000 tonnes par mois

Envoyer une demande de renseignements Chat en direct
  • Détails du produit

Le tube sans soudure en acier inoxydable ASTM A312 est un type de tube fabriqué en acier inoxydable et conçu pour être sans soudure, ce qui signifie qu'il ne comporte ni soudure, ni joint, ni raccord.

Ce type de tuyau est généralement utilisé dans des applications qui exigent un haut niveau de solidité, de durabilité et de résistance à la corrosion, notamment dans les secteurs de la chimie, du pétrole et du gaz, ainsi que de la pétrochimie.

La norme ASTM A312 définit les exigences relatives aux tubes en acier inoxydable austénitique sans soudure, soudés et fortement déformés à froid, destinés à des applications à haute température et à des environnements corrosifs en général. Cette norme couvre une gamme de nuances d'acier inoxydable, notamment les nuances 304, 316, 316L et 321.

ASTM A312 Tuyau sans soudure en acier inoxydable présente de nombreux avantages par rapport aux autres types de tuyaux. Par exemple, sa fabrication sans soudure élimine les points faibles de la canalisation, réduisant ainsi les risques de fuites et de fissures. Il résiste également aux températures et aux pressions élevées, ce qui le rend idéal pour les applications soumises à de fortes contraintes. De plus, l'acier inoxydable offre une excellente résistance à la corrosion et une grande durabilité, garantissant ainsi une longue durée de vie aux tuyaux.

En résumé, le tube sans soudure en acier inoxydable ASTM A312 est un type de tuyauterie de haute qualité, conçu pour être durable, solide et résistant à la corrosion. Il est utilisé dans un large éventail d'applications, notamment dans les secteurs de la chimie, du pétrole et du gaz, ainsi que de la pétrochimie. Sa construction sans soudure élimine les points faibles et garantit un système de tuyauterie fiable et durable.

 

Spécifications des tubes sans soudure en acier inoxydable
Caractéristiques techniquesASTM A 312 ASME SA 312
DimensionsASTM, ASME et API
Types de tubes en acier 310 ssSans couture
Diamètre extérieur (mm)de 6,00 à 610,00
Taille en NB1/8″ à 30″ NB
longueur en mm6 000, 3 000, 2 000, 12 000, ou selon les besoins
Épaisseur de la paroide 0,5 mm à 30 mm
Spécialisé dansGrand diamètre
Finition de la surfaceBrillant, décapé et recuit, poli, 2B, n° 4
Services à valeur ajoutéePolissage, chanfreinage, découpe, filetage
CalendrierAnnexe 20, Annexe 30, Annexe 40, STD, Annexe 80, XS, Annexe 60, Annexe 80, Annexe 120, Annexe 140, Annexe 160, XXS
FormulaireTubes carrés, tubes ronds, tubes rectangulaires, profilés en “ U ”, bobines plates, tubes enroulés, tubes hydrauliques
Rapports d'essais et contrôles par un organisme tiersCertificats d'essais en usine, rapports mécaniques, rapports d'essais PMI, rapports d'inspection visuelle, EN 10204 3.1, rapports d'analyse chimique, rapports d'inspection par un organisme tiers, rapports de laboratoire agréés par la NABL, rapports d'essais destructifs, rapports d'essais non destructifs
EmballageEmballés dans des caisses en bois, des sacs en plastique, en liasses avec des bandes d'acier, ou dans un emballage sur mesure
Réseau nationalWenzhou
 Tableau des dimensions des tubes en acier inoxydable ASTM A312 (en pouces)
TUYAU
TAILLE		O.D.
POUCES		5S510S10203040S et STD.4060Les années 80 et E.H.80100120140160DBL.
E.H.
1/8.405.035
.1383		.049
.1363		.049
.1363		.068
.2447		.068
.2447		.095
.3145		.095
.3145
1/4.540.049
.2570		.065
.3297		.065
.3297		.088
.4248		.088
.4248		.119
.5351		.119
.5351
3/8.675.049
.3276		.065
.4235		.065
.4235		.091
.5676		.091
.5676		.126
.7388		.126
.7388
1/2.840.065
.5383		.065
.5380		.083
.6710		.083
.6710		.109
.8510		.109
.8510		.147
1.088		.147
1.088		.187
1.304		.294
1.714
3/41.050.065
.6838		.065
.6838		.083
.8572		.083
.8572		.113
1.131		.113
1.131		.154
1.474		.154
1.474		.218
1.937		.308
2.441
11.315.065
.8678		.065
.8678		.109
1.404		.109
1.404		.133
1.679		.133
1.679		.179
2.172		.179
2.172		.250
2.844		.358
3.659
1 1/41.660.065
1.107		.065
1.107		.109
1.806		.109
1.806		.140
2.273		.140
2.273		.191
2.997		.191
2.997		.250
3.765		.382
5.214
1 1/21.900.065
1.274		.065
1.274		.109
2.085		.109
2.085		.145
2.718		.145
2.718		.200
3.631		.200
3.631		.281
4.859		.400
6.408
22.375.065
1.604		.065
1.604		.109
2.638		.109
2.638		.154
3.653		.154
3.653		.218
5.022		.218
5.022		.344
7.462		.436
9.029
2 1/22.875.083
2.475		.083
2.475		.120
3.531		.120
3.531		.203
5.793		.203
5.793		.276
7.661		.276
7.661		.375
10.01		.552
13.70
33.500.083
3.029		.083
3.029		.120
4.332		.120
4.332		.216
7.576		.216
7.576		.300
10.25		.300
10.25		.438
14.32		.600
18.58
3 1/24.000.083
3.472		.083
3.472		.120
4.973		.120
4.973		.226
9.109		.226
9.109		.318
12.51		.318
12.51		.636
22.85
44.500.083
3.915		 .083
3.915		.120
5.613		.120
5.613		.237
10.79		.237
10.79		.337
14.98		.337
14.98		 .438
19.00		.531
22.51		.674
27.54
4 1/25.000 .247
12.54		.355
17.60
55.563.109
6.349		.109
6.349		.134
7.770		.134
7.770		.258
14.62		.258
14.62		.375
20.78		.375
20.78		.500
20.78		.625
32.96		.750
38.55
66.625.109
7.585		.109
7.585		.134
9.289		.134
9.289		.280
18.97		.280
18.97		.432
28.57		.432
28.57		.562
36.39		.719
43.35		.864
53.16
TUYAU
TAILLE		O.D.
POUCES		5S510S10203040S et STD.4060Les années 80 et E.H.80100120140160DBL.
E.H.
77.625.301
23.54		.500
38.04		.875
63.08
88.625.109
9.914		.109
9.914		.148
13.40		.148
13.40		.250
22.36		.277
24.70		.322
28.55		.322
28.55		.406
35.64		.500
43.39		.500
43.39		.594
50.95		.719
60.71		.812
67.76		.906
74.69		.875
72.42
99.625.342
33.91		.500
48.73
1010.75.134
15.19		.134
15.19		.165
18.70		.165
18.70		.250
28.04		.307
34.24		.365
40.48		.365
40.48		.500
54.74		.500
54.74		.594
64.43		.719
77.03		.844
82.29		1.000
104.1		1.125
115.6		1.000
104.1
1111.75.375
45.56		.500
60.08
1212.75.156
21.07		.165
22.18		.180
24.16		.180
24.16		.250
33.38		.330
43.77		.375
49.56		.406
53.52		.562
73.15		.500
65.42		.688
88.63		.844
107.3		1.000
125.5		1.125
136.7		1.312
160.3		1.000
125.5
1414.00.156
23.07		.188
27.73		.250
36.71		.312
45.61		.375
54.57		.375
54.57		.438
63.44		.594
85.05		.500
72.09		.750
106.1		.938
130.9		1.094
150.8		1.250
170.2		1.406
189.1
1616.00.165
27.90		.188
31.75		.250
42.05		.312
52.27		.375
62.58		.375
62.58		.500
82.77		.656
107.5		.500
82.77		.844
136.6		1.031
164.8		1.219
192.4		1.438
223.6		1.594
245.3
1818.00165
31.43		.188
35.76		.250
47.39		.312
58.94		.438
82.15		.375
70.59		.562
104.7		750
138.2		.500
93.45		.938
170.9		1.156
208.0		1.375
244.1		1.562
274.2		1.781
308.5
2020.00.188
39.78		.218
46.05		.250
52.73		.375
78.60		.500
104.1		.375
78.60		.594
123.1		.812
166.4		.500
104.1		1.031
208.9		1.281
256.1		1.500
296.4		1.750
341.1		1.969
379.2
2424.00.218
55.37		.250
63.41		.250
63.41		.375
94.42		.562
140.7		.375
94.42		.688
171.3		.969
238.4		.500
125.5		1.219
296.8		1.531
367.4		1.812
429.4		2.062
483.1		2.344
542.1
2626.00.312
85.60		.500
136.17		.375
102.63		.500
136.17
2828.00.312
92.26		.500
146.85		.625
182.73		.375
110.64
3030.00.250
79.43		.312
98.93		.312
98.93		.500
157.53		.625
196.08		.375
118.65		.500
157.53
3232.00.312
105.59		.500
168.21		.625
209.43		.375
126.66		.688
230.08		.500
168.21
3434.00.312
112.25		.500
178.89		.625
222.78		.375
134.67		.688
244.77
3636.00.312
118.92		.500
189.57		.625
236.13		.375
142.68		.750
282.35
Tubes en acier inoxydable A312 : exigences relatives à la composition chimique
GradeUNSComposition, %
ConceptionCMnPSSiCrNiMoTiNbTaNVnCuCeBAlAutres
TP304S304000.0820.0450.03118.0–208.0–11. . .. . .. . .. . .. . .. . .. . .. . .
TP304LS304030.03520.0450.03118.0–208.0–13. . .. . .. . .. . .. . .. . .. . .. . .
TP304HS304090.04 – 0.120.0450.03118.0–208.0–11. . .. . .. . .. . .. . .. . .. . .. . .
TP310SS310080.0820.0450.03124.0- 2619.0- 220.75. . .. . .. . .. . .. . .. . .. . .
TP310HS310090.04 – 0.120.0450.03124.0–2619.0–22. . .. . .. . .. . .. . .. . .. . .
TP310HS310350.04 – 0.10.60.0250.0150.421.5–23.523.5–26.5. . .. . .0.40- 0.6. . .0.20- 0.3. . .2.5- 3.5. . .0.002- 0.008Voir les spécifications
TP316S316000.0820.0450.03116.0–1810.0–142.00–3. . .. . .. . .. . .. . .. . .. . .
TP316LS316030.03520.0450.03116.0–1810.0–142.00–3. . .. . .. . .. . .. . .. . .. . .
TP316HS316090.04 – 0.120.0450.03116.0–1810.0–142.00–3. . .. . .. . .. . .. . .. . .. . .
TP317S317000.0820.0450.03118.0–2011.0–153.0–4. . .. . .. . .. . .. . .. . .. . .
TP317LS317030.03520.0450.03118.0–2011.0–153.0–4. . .. . .. . .. . .. . .. . .. . .
TP321S321000.0820.0450.03117.0–199.0–12. . .Ti 5 × (C+N) min, 0,70 max. . .. . .0.1. . .. . .. . .
TP321HS321090.04 – 0.120.0450.03117.0–199.0–12. . .4 (C+N) min ; 0,70 max. . .. . .0.1. . .. . .. . .
TP321HS326540.022.0-40.030.0050.524.0–2521.0–237.0-8. . .. . .. . .0.45- 0.55. . .0.30-0.6. . .
TP321HS332280.04 – 0.0810.020.0150.326.0–2831.0–33. . .. . .0.60- 1. . .. . .. . .. . .0.05 – 0.10.025
TP321HS345650.035.0-70.030.01123.0–2516.0–184.0-5. . .0.1. . .0.40- 0.6. . .. . .. . .
TP347S347000.0820.0450.03117.0–199.0–13. . .. . .Voir les spécifications. . .. . .. . .. . .. . .
TP347HS347090.04 – 0.120.0450.03117.0–199.0–13. . .. . .Voir les spécifications. . .. . .. . .. . .. . .
Alliage 20N080200.0720.0450.035119.0–2132.0–382.0–3. . .Voir les spécificationsVoir les spécifications. . .. . .3.0– 4. . .. . .. . .
Alliage 20N083670.0320.040.03120.0–2223.5–25.56.0–7. . .. . .. . .0.18–0.25. . .0.75. . .. . .. . .
Alliage 20N080280.032.50.030.03126.0–2830.0–343.0–40.60–1.4
Alliage 20N080290.0220.0250.0150.626.0–2830.0–344.0–50.6– 1.4

Le tube doit être fabriqué selon l'un des procédés suivants : sans soudure (SML), soudé (WLD) ou fortement déformé à froid (HCW).

Normes de référence ASTM

A262 Méthodes de détection de la sensibilité à la corrosion intergranulaire dans les aciers inoxydables austénitiques
A370 Méthodes d'essai et définitions relatives aux essais mécaniques des produits en acier
A941 Terminologie relative à l'acier, à l'acier inoxydable, aux alliages apparentés et aux ferroalliages
A999/A999M Cahier des charges relatif aux exigences générales concernant les alliages et Tube en acier inoxydable
A1016/A1016M Spécifications relatives aux exigences générales applicables aux tubes en acier allié ferritique, en acier allié austénitique et en acier inoxydable
E112 Méthodes d'essai pour la détermination de la granulométrie moyenne
E381 Méthode d'essai par macro-gravure des barres d'acier, des billettes, des blooms et des pièces forgées
E527 Pratique relative à la numérotation des métaux et des alliages dans le système de numérotation unifié (UNS)

Spécifications standard :
  • ASTM A213 / A213M – 11a : Spécification standard relative aux tubes sans soudure en acier allié ferritique et austénitique destinés aux chaudières, surchauffeurs et échangeurs de chaleur
  • ASTM A269 – 10 : Spécification standard relative aux tubes en acier inoxydable austénitique sans soudure et soudés destinés à un usage général
  • ASTM A312 / A312M – 12 : Spécification standard relative aux tubes en acier inoxydable austénitique sans soudure, soudés et fortement déformés à froid
  • ASTM A511 / A511M – 12 : Spécification standard relative aux tubes mécaniques sans soudure en acier inoxydable
  • ASTM A789 / A789M – 10a : Spécification standard relative aux tubes en acier inoxydable ferritique/austénitique, sans soudure et soudés, destinés à un usage général
  • ASTM A790 / A790M – 11 : Spécification standard relative aux tubes en acier inoxydable ferritique/austénitique, sans soudure et soudés
  • DIN 17456-2010 : TUBES CIRCULAIRES SANS SOUDURE EN ACIER INOXYDABLE À USAGE GÉNÉRAL.
  • DIN 17458-2010 : Tubes circulaires sans soudure en acier inoxydable austénitique
  • EN 10216-5 CT 1/2 : Tubes sans soudure en acier inoxydable
  • GOST 9941-81 : TUBES SANS SOUDURE, FORGÉS À FROID ET À CHAUD, EN ACIER RÉSISTANT À LA CORROSION.
Propriétés mécaniques
TempérerRecuitÉtabli à froid (environ 20%)
Matériau316316L316316L
Résistance à la traction Rm7570ksi (min)102-131ksi (min)
Résistance à la traction Rm515485MPa (min)700-900MPa (min)
R.p. 0.2% Rendement3027ksi (min)73-102ksi (min)
R.p. 0.2% Rendement205182MPa (min)500-700MPa (min)
Allongement (2” ou 4D gl)35% (min)40% (min)
Propriétés physiques (à température ambiante)
Chaleur spécifique (0-100°C)500J.kg-1.°K-1
Conductivité thermique16.3W.m -1.°K-1
Dilatation thermique15.9μm/μm/°C
Module d'élasticité193GPa
Résistivité électrique7.4μohm/cm
Densité7.99g/cm3
Applications et utilisations des tubes sans soudure en acier inoxydable
  • Installations de conversion d'énergie
  • Tubes radiants
  • Muffles, réacteurs, couvercles de recuit
  • Composants internes d'un gazéificateur de charbon
  • Saggers
  • Supports de tubes pour raffineries de pétrole et chaudières à vapeur
  • Pièces de four, bandes transporteuses, rouleaux, revêtements de four, ventilateurs
  • Équipement de transformation des aliments
    • Structures cryogéniques
    • Équipements pour fours industriels
    • Équipements pour l'industrie pétrolière
    • Paniers pour traitement thermique
    • Chaudières à vapeur et puits thermométriques
    • Industries du fer, de l'acier et des métaux non ferreux
    • Secteur de l'ingénierie
  • Fours
  • Échangeurs de chaleur
  • Industrie du ciment
Prix des tubes sans soudure en acier inoxydable ASTM TP310S
ProduitPrix en ($)
• Tuyau sans soudure SS 310, norme ASTM A312, TP 310$ 10 000 ~ $ 11 500 USD/tonne
• Tuyau sans soudure SS 310S, conforme à la norme ASTM A312 TP 310S$ 10 500 ~ $ 12 000 USD/tonne
• Tuyau SS 310 ERW/soudé, conforme à la norme ASTM A312 TP 310$ 9 000 ~ $ 10 500 USD/tonne
• SS 310S ERW / Tuyau soudé ASTM A312 TP 310S$ 9 500 ~ $ 11 000 USD/tonne
• Tuyau SS 310 EFW conforme à la norme ASTM A358 TP 310$ 8 800 ~ $ 10 000 USD/tonne
• Tuyau SS 310S EFW conforme à la norme ASTM A358 TP 310S$ 9 000 ~ $ 10 500 USD/tonne
Prix des tubes en acier inoxydable 310/310S
ProduitPrix en ($)
• Tube sans soudure SS 310 / Tuyau ASTM A269 TP 310$ 11 000 ~ $ 13 500 USD/tonne
• Tube sans soudure SS 310S / Tubes ASTM A269 TP 310S$ 11 500 ~ $ 13 080 USD/tonne
• SS 310 ERW / Tube soudé / Tubes ASTM A249 TP 310$ 10 500 ~ $ 15 000 USD/tonne
• SS 310S ERW / Tube soudé / Tubes ASTM A249 TP 310S$ 11 000 ~ $ 12 500 USD/tonne
• Tubes d'échangeur de chaleur SS 310 / Tubulerie ASTM A213 TP 310$ 11 500 ~ $ 13 500 USD/tonne
• Tubes et tuyaux d'échangeur de chaleur SS 310S, conformes à la norme ASTM A213 TP 310S$ 11 500 ~ $ 13 500 USD/tonne
• Tube sans soudure recuit brillant SS 310 / Tubes ASTM A269 TP 310$ 11 500 ~ $ 13 500 USD/tonne
• Tube sans soudure recuit brillant SS 310S / Tubes ASTM A269 TP 310S$ 11 500 ~ $ 13 500 USD/tonne
Prix des tubes sans soudure en acier inoxydable
ProduitPrix en ($)
• Tube sans soudure SS 321 / Tubes ASTM A269 TP 321$ 6 400 ~ $ 7 900 USD/tonne
• Tube sans soudure SS 321H / Tubes ASTM A269 TP 321H$ 6 500 ~ $ 8 000 USD/tonne
• SS 321 ERW / Tube soudé / Tubes ASTM A249 TP 321$ 5 900 ~ $ 7 400 USD/tonne
• SS 321H ERW / Tube soudé / Tubes ASTM A249 TP 321H$ 6 000 ~ $ 7 500 USD/tonne
• SS 321 : Tubes et tuyaux pour échangeurs de chaleur, norme ASTM A213 TP 321$ 6 400 ~ $ 7 900 USD/tonne
• SS 321H : tubes et tuyaux pour échangeurs de chaleur, conformes à la norme ASTM A213 TP 321H$ 6 400 ~ $ 7 900 USD/tonne
• Tube sans soudure recuit brillant SS 321 / Tubulure ASTM A269 TP 321$ 6 400 ~ $ 7 900 USD/tonne
• Tube sans soudure recuit brillant SS 321H / Tubes ASTM A269 TP 321H$ 6 400 ~ $ 7 900 USD/tonne
Tags :

Prev :

Suivant :

Produits apparentés

+86-577-85980211

+8613587625968

306208216

Laisser un message

    Please prove you are human by selecting the plane.