316Lstainlesssteel1.4404(UNS31603)中国制造

不锈钢级

什么是不锈钢 316L (我们 31603)1.4404?

1.4404 is an acid-resisting austenitic stainless steel with 17% 铬, 12% Ni and 2,0% 莫. Due to its Mo content, this material has a significantly improved corrosion resistance compared to stainless steels. 1.4404 is resistant to reducing action of organic and inorganic acids as well as against halogen-containing media. 此外, this steel is less susceptible to pitting. The low carbon content also improves the resistance to intergranular corrosion and allows use at higher temperatures up to 450 ° C in continuous operation. 1.4404 can be cold worked and weld excellent. This material is mainly used in the chemical, textile and paper industries, and is often used in apparatus, in sanitary industry and in pipe fabrication.

Equivalent Grades of Stainless Steel 1.4404

欧洲联盟
美国
德国
从,WNr
日本
法国
AFNOR
英格兰
学士
意大利
大学
中国
国标
瑞典
SS
波兰
PN
捷克
南航
芬兰
超短距离飞行系统
奥地利
奥诺玛
Inter
国际标准化组织
X2CrNiMo17-12-2 (1.4404)316LX2CrNiMo17-13-2SUS316SUS316LZ2CND17-12Z3CND17-11-02Z3CND18-12-02316S11X2CrNiMo17-12X2CrNiMo17-17-1200Cr17Ni14Mo20Cr18Ni12Mo2Ti2348 00H17N13M200H17N14M217349 750 X2CrNiMo17-13-2KKWType19
SS 1.4404 化学成分(%)
CS
% % % % %%%% %
0,031,02,00,0450,01516,5-18,52,0-2,510,0-13,00,11

机械性能 

The values given refer to the diameter range ≤ 160 (Ø in mm) 和 160 < d ≤ 250 (Ø in mm)*

Hardness in HB: 215

Yield strength Rp0.2 in Mpa: ≥ 200

Yield strength Rp1.0 in Mpa: ≥ 235

Strength / tensile strength Rm in Mpa: 500-700

Elongation at break A in % (longitudinal) at ≤ 160: ≥ 40

* These figures refer to mechanical properties at room temperature in the solution-annealed state (according to EN 10088-3)

物理特性
Density in kg/dm38,0
Thermal conductivity at 20°C in W/(m K)15
Electr. Resistance at 20°C (Ω mm2 /m)0,75
Specific heat capacity at 20°C (J/kg K)500
Supplied Forms

床单;条;管子;酒吧;管道;盘子;配件 & 法兰;Angle.

耐腐蚀性能

Due to the low carbon content, the material 1.4404 is resistant to intercrystalline corrosion but not sea water resistant. In natural environmental media and moderate concentrations of chlorine and salt, this grade of material has excellent corrosion resistance.

制造

所有不锈钢的制造只能使用不锈钢材料专用的工具来完成. 使用前必须彻底清洁工具和工作表面. 这些预防措施对于避免不锈钢被容易腐蚀的金属交叉污染是必要的,这些金属可能会使制成品的表面变色.

热处理
316L stainless steel  1.4404Heat Treatment
316L stainless steel 1.4404Heat Treatment
冷加工

年级 316 is readily brake or roll formed into a variety of parts. It is also suited to stamping, heading and drawing but post work annealing is recommended to relieve internal stresses.

Cold working will increase both strength and hardness of 316 不锈钢.

热加工

All common hot working processes can be performed on 316 不锈钢. Hot working should be avoided below 927°C. The ideal temperature range for hot working is 1149-1260°C. Post-work annealing is recommended to ensure optimum corrosion resistance.

机械加工性

AISI 316L stainless steel has medium machinability. In direct comparison, the machinability of this stainless steel grade is better than that of 美国钢铁协会 316/1.4401 due to its lower carbon content.

焊接

AISI 316L stainless steel (1.4404 / X2CrNiMo17-12-2) has excellent weldability. The material can be used with all common welding methods (with the exception of gas welding). The addition of a welding filler metal and subsequent heat treatment are not normally required. Resistance to intergranular corrosion is not affected by welding.

应用领域
  • Pulp and paper equipment;
  • Heat exchanger;
  • Dyeing equipment;
  • Film processing equipment;
  • Pipeline;
  • Materials for exterior construction in coastal areas;
  • Watch bracelet, case, ETC. for advanced watches;
  • Equipment for the use of marine, chemicals, dyes, 纸, oxalic acid, fertilizer, ETC。;
  • Food industry;
  • Rope;
  • CD pole;
  • Bolts and nuts;