316L stainless steel 1.4404 (نحن 31603)

What is stainless steel 316ل (نحن 31603)1.4404?

1.4404 is an acid-resisting austenitic stainless steel with 17% سجل تجاري, 12% Ni and 2,0% شهر. Due to its Mo content, this material has a significantly improved corrosion resistance compared to stainless steels. 1.4404 is resistant to reducing action of organic and inorganic acids as well as against halogen-containing media. بالإضافة إلى, this steel is less susceptible to pitting. The low carbon content also improves the resistance to intergranular corrosion and allows use at higher temperatures up to 450 ° C in continuous operation. 1.4404 can be cold worked and weld excellent. This material is mainly used in the chemical, textile and paper industries, and is often used in apparatus, in sanitary industry and in pipe fabrication.

Equivalent Grades of Stainless Steel 1.4404

الاتحاد الأوروبي في

الولايات المتحدة الأمريكية –

ألمانيا من,WNr

اليابان هو

فرنسا أفنور

إنكلترا بكالوريوس

إيطاليا UNI

الصين غيغابايت

السويد SS

بولندا PN

التشيك CSN

فنلندا SFS

النمسا ONORM

Inter ايزو

X2CrNiMo17-12-2 (1.4404)

316ل

X2CrNiMo17-13-2

SUS316SUS316L

Z2CND17-12Z3CND17-11-02Z3CND18-12-02

316S11

X2CrNiMo17-12X2CrNiMo17-17-12

00Cr17Ni14Mo20Cr18Ni12Mo2Ti

2348

00H17N13M200H17N14M2

17349

750

X2CrNiMo17-13-2KKW

Type19

SS 1.4404 Chemical Composition(%)

ج	و	مينيسوتا	ص	س	سجل تجاري	شهر	في	ن
≤ %	≤ %	≤ %	≤ %	≤ %	%	%	%	≤ %
0,03	1,0	2,0	0,045	0,015	16,5-18,5	2,0-2,5	10,0-13,0	0,11

الخصائص الميكانيكية 

The values given refer to the diameter range ≤ 160 (Ø in mm) و 160 < d ≤ 250 (Ø in mm)*

Hardness in HB: ≤ 215

Yield strength Rp0.2 in Mpa: ≥ 200

Yield strength Rp1.0 in Mpa: ≥ 235

Strength / tensile strength Rm in Mpa: 500-700

Elongation at break A in % (longitudinal) at ≤ 160: ≥ 40

* These figures refer to mechanical properties at room temperature in the solution-annealed state (according to EN 10088-3)

الخصائص الفيزيائية

Density in kg/dm3	8,0
Thermal conductivity at 20°C in W/(m K)	15
Electr. Resistance at 20°C (Ω mm2 /m)	0,75
Specific heat capacity at 20°C (J/kg K)	500

Supplied Forms

Sheet;Strip;أنبوب;Bar;ماسورة;Plate;Fittings & Flanges;Angle.

المقاومة للتآكل

Due to the low carbon content, the material 1.4404 is resistant to intercrystalline corrosion but not sea water resistant. In natural environmental media and moderate concentrations of chlorine and salt, this grade of material has excellent corrosion resistance.

Fabrication

Fabrication of all stainless steels should be done only with tools dedicated to stainless steel materials. Tooling and work surfaces must be thoroughly cleaned before use. These precautions are necessary to avoid cross contamination of stainless steel by easily corroded metals that may discolour the surface of the fabricated product.

المعالجة الحرارية

Cold Working

درجة 316 is readily brake or roll formed into a variety of parts. It is also suited to stamping, heading and drawing but post work annealing is recommended to relieve internal stresses.

Cold working will increase both strength and hardness of 316 الفولاذ المقاوم للصدأ.

Hot Working

All common hot working processes can be performed on 316 الفولاذ المقاوم للصدأ. Hot working should be avoided below 927°C. The ideal temperature range for hot working is 1149-1260°C. Post-work annealing is recommended to ensure optimum corrosion resistance.

آلية

AISI 316L stainless steel has medium machinability. In direct comparison, the machinability of this stainless steel grade is better than that of AISI 316/1.4401 due to its lower carbon content.

اللحام

AISI 316L stainless steel (1.4404 / X2CrNiMo17-12-2) has excellent weldability. The material can be used with all common welding methods (with the exception of gas welding). The addition of a welding filler metal and subsequent heat treatment are not normally required. Resistance to intergranular corrosion is not affected by welding.

Applications

• Pulp and paper equipment;
• Heat exchanger;
• Dyeing equipment;
• Film processing equipment;
• Pipeline;
• Materials for exterior construction in coastal areas;
• Watch bracelet, case, إلخ. for advanced watches;
• Equipment for the use of marine, chemicals, dyes, paper, oxalic acid, fertilizer, إلخ.;
• Food industry;
• Rope;
• CD pole;
• Bolts and nuts;