416 Stainless steel 1.4005（UNS41600）

What is stainless steel 416？

416 is a 400 series martensitic stainless steel that offers the best machinability (85%) of all stainless steel, primarily composed of chromium, แมงกานีส, and sulfur. The material complies with the ASTM A582 standard and is equivalent to EN 1.4005 (X12CrS13) and UNS S41600. Its superior machinability comes from its high sulfur content, making it especially suitable for high-speed machining operations. อย่างไรก็ตาม, the addition of sulfur also reduces its formability, weldability, and corrosion resistance. Common applications include components such as screws, bolts, and pump shafts, where ease of machining and moderate corrosion resistance are required.

416 สแตนเลส 1.4005 Finished Products Form

Sheet, Strip, จาน – Inquiry with Ulbrich Stainless Steel Sales Wire – Profile, Round, Square Rectangular cross sections – Inquiry with Ulbrich Shaped Wire Sales

Applications for 416 สแตนเลส

• Electrical motors
• Nuts and bolts
• Pumps
• Valves
• Automatic screw machine parts
• Washing machine components
• Studs
• Gears

อีquivalents of grade 416

ระดับ	UNS No	Old British		Euronorm		Swedish SS	Japanese JIS
		BS	En	เลขที่	ชื่อ
416	S41600	416S21	56AM	1.4005	X12CrS13	2380	SUS 416

416 Stainless steel 1.4005（UNS41600）Chemical Composition

ระดับ	ค, สูงสุด	มน, สูงสุด	และ, สูงสุด	ป, สูงสุด	ส, นาที	Cr	Mo, สูงสุด
416	0.15	1.25	1.00	0.06	0.15	12-14	0.6

คุณสมบัติทางกล 

Tempering Temperature (° C)	Tensile Strength (MPA)	Yield Strength 0.2% Proof (MPA)	การยืดตัว (% in 50mm)	Hardness Brinell (HB)
อบอ่อน *	517	275	30	262
Condition T **	758	586	18	248-302
204	1340	1050	11	388
316	1350	1060	12	388
427	1405	1110	11	401
538	1000	795	13	321
593	840	705	19	248
650	796	670	17.5	253

* Annealed properties are typical for Condition A of ASTM A582.
** Hardened and tempered Condition T of ASTM A582 – Brinell hardness is specified range, other properties are typical only.
# Tempering of this steel at temperatures of 400 to 580°C should be avoided due to low impact resistance.

416 Stainless steel 1.4005（UNS41600）คุณสมบัติทางกายภาพ

Corrosion Resistance

• Demonstrates corrosion resistance to natural food acids, waste products, basic and neutral salts, natural waters, and most atmospheric conditions
• Less resistant that the austenitic grades of stainless steel and also the 17% chromium ferritic alloys
• High sulfur, free-machining grades like Alloy 416 are unsuitable for marine or other chloride exposure
• Maximum corrosion resistance is achieved in the hardened condition, with a smooth surface finish

Heat Resistance

Scaling resistance of grade 416 steels under intermittent conditions can be extended up to 760°C, and up to 675°C under continuous operations. Considering the sustainability of mechanical properties, 416 steels should not be employed at temperatures greater than the standard tempering temperatures.

Heat Treatment

• Annealing: Heat to 815-900°C, followed by slow furnace cooling.
• Hardening: Heat to 950-1020°C, then quench in oil or air.
• Tempering: Heat to 205-370°C, then air cool.

Welding

ระดับ 416 steel exhibits poor weldability. Welding can be carried by pre-heating 416 steels to 200 to 300°C, followed by re-hardening, annealing or stress relieving at 650 to 675°C.

Machinability

Speeds and feed comparable with those of some of the free machining carbon steels. Good chip breakage. Material heat treated at 200 F and cold drawn will give best results.