வென்ஷோ கெய்சின் கெய்சின் மெட்டல் கோ., லிமிடெட்
What is stainless steel 317LN？
Stainless steel 317LN is a nitrogen alloyed austenitic stainless steel having high nitrogen content than other austenitic stainless steels. It has higher yield and tensile strength than 317எல். This low carbon grade steel provides resistance to sensitization during welding and thermal processes. Low carbon content in its composition makes the alloy resistant to inter granular corrosion. It also offers excellent corrosion resistance to organic, sulfuric and phosphoric acids.
317LN துருப்பிடிக்காத எஃகு 1.4434 Finished Products Form
- Coil – Strip
- Foil: Inquire with Ulbrich Stainless Steel Wire – Profile
- Round
- Flat
- Square
Applications for 317LN துருப்பிடிக்காத எஃகு
- Chemical processing equipment
- Food processing equipment
- Pharmaceutical manufacturing equipment
- Marine engines and exhaust systems
- Offshore drilling platforms
- Aerospace components
- Power generation equipment
- Heat exchangers
- Boilers
- Turbines
- Piping systems
- Reactors
- Tanks
- Valves
- Springs
Equivalents of grade 317LN
| JIS G4304 | ASTM | UNS | KS | ISO Designation | AISI |
| SUS317LN | 317LN | S31753 | STS317LN | X2CrNiMoN18-12-4 | 317LN |
Chemical Composition
| Elements | Fe | Cr | Ni | Mo | Mn | Si | N | பி | C | எஸ் |
| Min (%) | 57.9 | 18 | 11 | 3.0 | – | – | 0.1 | – | – | – |
| Max (%) | 67.9 | 20 | 15 | 4.0 | 2.0 | 0.75 | 0.22 | 0.045 | 0.030 | 0.030 |
Mechanical Properties
| Properties | Metric | Imperial |
| Tensile strength | ≥590 MPa | ≥85600 psi |
| Yield strength | ≥285 MPa | ≥41300 ksi |
| Modulus of elasticity | 200 GPa | 29000 ksi |
| Shear modulus | 77 GPa | 11200 ksi |
| Poissons ratio | 0.299 | 0.299 |
| Elongation at break | ≥40% | ≥40% |
Physical Properties
Manufacturing process
The properties of 317LN is similar to other conventional austenitic stainless steels, and can therefore, be fabricated in a manner similar to alloys 316எல் and 317L. Heat treatment of 317LN can be carried out at temperatures ranging from 1080 to1175°C (1975 to 2150°F) followed by rapid water quenching. This grade is not hardenable.