Wenzhou Kaixin Kaixin Metal Co., Ltd
Alloy Steel is steel that is alloyed with a variety of elements in total amounts between 1.0% 그리고 50% by weight to improve its mechanical properties. Alloy steels are broken down into two groups: low-alloy steels and high-alloy steels. The difference between the two is somewhat arbitrary: Smith and Hashemi define the difference at 4.0%, while Degarmo, et al., define it at 8.0%. Most commonly, the phrase “합금강 ” refers to low-alloy steels. Strictly speaking, every steel is an alloy, but not all steels are called “alloy steels”. The simplest steels are iron (Fe) alloyed with carbon (기음) (about 0.1% 에게 1%, depending on type). 하지만, the term “합금강 ” is the standard term referring to steels with other alloying elements added deliberately in addition to the carbon. Common alloyants include manganese (the most common one), nickel, 크롬, molybdenum, vanadium, silicon, and boron. Less common alloyants include aluminum, cobalt, copper, cerium, niobium, titanium, tungsten, tin, zinc, lead and zirconium.
ASTM A335 P11 Specification
| ASME SA335 P11 Pipe Standard | ASTM A335 P11, SA335 P11 (with IBR Test Certificate) |
|---|---|
| ASTM A335 Grade P11 Pipe Size | 1/2” NB to 36” NB |
| A335 Grade P11 Pipe Thickness | 3-12mm |
| ASME SA335 P11 Pipe Schedules | Sch 5, SK10, Sch 40, Sch 80, Sch 80s, Sch 160, SCH XXS, SCH XS, All Schedules |
| ASTM A335 Grade P11 Pipe 용인 | Cold drawn pipe: +/-0.1mm
Cold rolled pipe: +/-0.05mm
|
| Craft | Cold rolled and Cold drawn |
| ASME SA335 P11 Pipe Type | 원활한 / 에이커 / 용접됨 / 만드는 |
| A335 Grade P11 Pipe available in Form of | Rectangular, 둥근, Square, Hydraulic Etc. |
| ASTM A335 Grade P11 Pipe Length | 기준 Double & In Cut length also. |
| ASME SA335 P11 Pipe End | Beveled End,Plain End, Treaded |
| Specialized in | Large Diameter A335 Grade P11 Pipe |
| Additional Testing | NACE TM0284, NACE MR 0175, NACE TM0177, HIC TEST, SSC TEST, H2 SERVICE, IBR, 등. |
| 애플리케이션 | Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service |
| Alloy Steel P11 Pipe Origin | 중국 |
ASTM A335 Grade P91 Alloy Steel Pipe Chemical Compositions :
| 기음, % | MN, % | 피, % | 에스, % | 그리고, % | Cr, % | 모, % | V, % | N, % | ~ 안에, % | Al, % | Nb, % |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 0.08-0.12 | 0.3-0.6 | 0.02 최대 | 0.01 최대 | 0.2-0.5 | 8.0-9.5 | 0.85-1.05 | 0.18-0.25 | 0.03-0.07 | 0.4 최대 | 0.04 최대 | 0.06-0.10 |
Alloy Steel P91 Seamless Pipes Mechanical Properties :
| 인장강도 , MPa | 항복 강도, MPa | 연장, % | 경도, HB |
|---|---|---|---|
| 585 min | 415 min | 20 min | 250 최대 |
ASME SA335 P11 Seamless Pipes
Standard Specification for Seamless Carbon Steel Pipe for High-Temperature Service
This specification2 covers nominal wall and minimum wall seamless ferritic alloy-steel pipe intended for high temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Selection will depend upon design, service conditions, 기계적 성질, and high-temperature characteristics.
ASTM A335 Pipe (ASME S/A335, Chorme-Moly) is a seamless ferritic Alloy-Steel Pipe for high temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Sometimes referred to as “P Grade”, Chrome Moly Pipe is popular in Stainless Steel Tubes P-Grades P5, P9, P11, P22, and P91. The most common use of grades P11, P22, and P91 is in the power industry and petro-chemical plants, Grades P5 and P9 are commonly used in refineries.
A335 is often called chrome moly pipe because of the chemical makeup of Molybdenum (모) and Chromium (Cr). Molybdenum increases the strength of steel as well as the elastic limit, resistance to wear, impact qualities, and hardenability. Moly increases the resistance to softening, restrains grain growth and makes chromium steel less susceptible to embrittlement. Moly is the most effective single additive that increases high temperature creep strength. It also enhances the corrosion resistance of steel, and inhibits pitting. 크롬 (or chrome) is the essential constituent of Stainless Steel. Any steel with 12% or more Chrome is considered stainless. Chrome is virtually irreplaceable in resisting oxidation at elevated temperatures. Chrome raises the tensile, yield, and P11 Material Hardness value at room temperatures. The composition chrome moly Alloy Steel pipe and Alloy Steel Tubes make it ideal for use in power plants, refineries, petro chemical plants, and oil field services where fluids and gases are transported at extremely high temperatures and pressures.