302HQ Stainless steel

What is stainless steel 302HQ？

Grade 302HQ is a specialised wire grade with very wide usage for manufacture of stainless steel

Pričvršćivači. The inclusion of 3% copper in the composition reduces the cold work hardening rate

substantially compared to Grade 304. 302HQ is standard for manufacture of self-tapping screws

and light machine screws; it is also used for some bolts, set screws, rivets and specialised

Pričvršćivači. It has now totally replaced Grades 384 i 305 for cold heading applications, copper

being a lower cost alternative to their high nickel contents.

The designation 302HQ is not standardised – ASTM specifications list the grade as UNS S30430,

and alternative designations for the same grade include “XM-7”, “304Cu” i “304HQ”. The

standard specification for stainless steel fasteners, ISO 3506, includes 302HQ as an acceptable

composition for fastener grade “A2”; it is commonly produced in strength grades A2-70 and A2-80.

302HQ nerđajući čelik 1.4567 Finished Products Form

• Coil – Strip
• Foil: Inquire with Ulbrich Stainless Steel Wire – Profile
• Okrugli
• Flat
• Square

Applications for 302HQ nerđajući čelik

• Oprema za preradu hrane
• Transport and storage equipment (e.g., beer brewing, prerada mlijeka, izrada vina)
• Kuhinjske klupe, sudoperi, korito, equipment, and appliances
• Architectural paneling, ograde, and trim
• Kemijski kontejneri, uključujući transport
• Heat exchangers
• Woven or welded screens
• Navojni pričvršćivači
• Springs

Equivalents of grade 302HQ

Ocjena	Nas br	Stari britanski		Euronorm		Švedski SS	Japanski on
		BS	U	br	Ime
302HQ	S30430	394S17	–	1.4567	X3CrNiCu18-9-4	–	SUS XM7

Sastav ranges for 302HQ grade of stainless steel

Mehanička svojstva 

Property	Value
Zatezna čvrstoća, min	515 MPa
Snaga prinosa (0.2% Proof), min	205 MPa
Elongation in 50 mm, min	40%
Tvrdoća, max	201 HB

Fizička svojstva

Ocjena	Gustina (kg / m3)	Elastični modul (GPA)	Srednji koeficijent termičkog širenja (µm/m/°C)			Toplotna provodljivost (W / m.k)		Specifična toplina 0-100 °C (J / kg.k)	Električna otpornost (nω.m)
			0-100 °C	0-315 °C	0-538 °C	at 100 °C	at 500 °C
302HQ	8027	193	17.2	17.8	18.8	16.3	21.5	500	720

Otpornost na koroziju

Equal to or exceeding that of Ocjena 304. Subject to pitting and crevice corrosion in warm chloride

environments, and to stress corrosion cracking above about 50°C. 302HQ is considered resistant

to potable water with up to about 200mg/L chlorides at ambient temperatures, reducing to about

150mg/L at 60°C.

Heat Resistance

Good oxidation resistance in intermittent service to 870°C and in continuous service to 925°C.

Continuous use of Grade 302HQ in 425-860°C range is usually safe (free of carbide precipitation)

as the grade has a very low carbon content.

Toplotni tretman

Solution Treatment (Annealing) – Heat to 1010-1120°C and cool rapidly. This grade cannot be hardened by thermal treatment.

Cold Work Hardening

302HQ has the lowest work hardening rate of any of the common austenitic stainless steels. This results in a tensile strength increase of approximately 8MPa/%Ra (8MPa increase in tensile strength for each 1% reduction of area of cold work – this data from wire drawing). Even after substantial cold work this grade remains essentially non-responsive to a magnet.

Zavarivanje

Stainless steel AISI 304CU (1.4567, X3CrNiCu18-9) has good weldability and can be used with many common welding processes such as TIG welding and MIG welding. It can also be used for arc welding, but this should be carried out with appropriate welding parameters to avoid overheating and distortion. To reduce tension and maintain the mechanical properties, the material should be allowed to cool in the air after welding. No heat treatment is required.

Machinability

AISI 304CU (1.4567) stainless steel is generally machinable, but this material hardens during machining. Stoga, care must be taken to select a sufficient cutting depth. In addition, suitable tools and coolants should be used to prevent overheating and extend tool life.